ADC foaming agent
產(chǎn)品中心
ST
Model: ST
Main chemical composition: Azodicarbonamide
Product features: Light yellow crystalline powder, large Amount of gas evolution, low coat and high cost performance
Technical indexes: Decomposition temperature: 205±3ºC
Amount of gas evolution: 225±5ml/g(STP)
Average particle size(D50): 11-12μm
Application:
Common universal high temperature foaming agent for PVC, PS, PP, PE. Widely used in plastics and rubber foam, such as PE, PS, EVA PVC, NBR, SBR. Especially suitable for PE mold foam; Commonly used in large mold pressing and PVC EVA molded foam; it can be used for rubber molded foam or free mold
Packing: 25kg lined with plastic bag.
Storage: Good storage stability at room temperature. It should be stored in a cool & dry place, away from fire, sparks and heat. In case of fire, please use spray water, carbon dioxide or chemical powder for fire extinguishing, no artificial fight.
ST-102
Model: ST-102
Main chemical composition: Azodicarbonamide
Product features: Light yellow crystalline powder, small Average particle size, and narrow distribution, fine and uniform cell, high expansion ratio, uniformly dispersed in plastic.
Technical indexes: Decomposition temperature: 205±3ºC
Amount of gas evolution: 225±5ml/g(STP)
Average particle size(D50): 3-4μm
Application: Widely used in rubber and plastic products with higher requirements, such as high-density EVA PE shoe materials, PVC / NBR rubber insulation materials, auto parts. Especially suitable for the free foam of PVC / NBR rubber insulation material, commonly used in the extrusion of EVA MD granulated injection, molding foam of PE, PVC molding, extrusion and coating, as well as molding, extrusion and coating of rubber plastic and rubber.
Packing: 25kg lined with plastic bag.
Storage: Good storage stability at room temperature. It should be stored in a cool & dry place, away from fire, sparks and heat. In case of fire, please use spray water, carbon dioxide or chemical powder for fire extinguishing, no artificial fight.
ST-103
Model: ST-103
Main chemical composition: Azodicarbonamide
Product features: Light yellow crystalline powder, small Average particle size, and narrow distribution, fine and uniform cell, high expansion ratio, uniformly dispersed in plastic.
Technical indexes: Decomposition temperature: 205±3ºC
Amount of gas evolution: 225±5ml/g(STP)
Average particle size(D50): 5-6μm
Application: Widely used in rubber and plastic products with higher requirements, such as high-density EVA PE shoe materials, PVC / NBR rubber insulation materials, auto parts. Especially suitable for the free foam of PVC / NBR rubber insulation material, commonly used in the extrusion of EVA MD granulated injection, molding foam of PE, PVC molding, extrusion and coating, as well as molding, extrusion and coating of rubber plastic and rubber.
Packing: 25kg lined with plastic bag.
Storage: Good storage stability at room temperature. It should be stored in a cool & dry place, away from fire, sparks and heat. In case of fire, please use spray water, carbon dioxide or chemical powder for fire extinguishing, no artificial fight.
ST-104
Model: ST-104
Main chemical composition: Azodicarbonamide
Product features: Light yellow crystalline powder, small Average particle size, and narrow distribution, fine and uniform cell, high amount of gas evolution, uniformly dispersed in plastic.
Technical indexes: Decomposition temperature: 205±3ºC
Amount of gas evolution: 225±5ml/g(STP)
Average particle size(D50): 7-8μm
Application: Common universal high temperature foaming agent. Widely used in plastics and rubber foam, such as PS, EVA, PVC, and NBR, SBR, and rubber mixture. Especially suitable for PVC calendering and coating; Commonly used in molded PE, PVC extrusion and rubber molded foam; can be used for the MD injection of EVA and large and small mold pressing foam. Widely used in insulation materials, sports equipment handle and shoe material.
Packing: 25kg lined with plastic bag.
Storage: Good storage stability at room temperature. It should be stored in a cool & dry place, away from fire, sparks and heat. In case of fire, please use spray water, carbon dioxide or chemical powder for fire extinguishing, no artificial fight.
ST-105
Model: ST-105
Main chemical composition: Azodicarbonamide
Product features: Light yellow crystalline powder, small Average particle size, and narrow distribution, fine and uniform cell, high amount of gas evolution, uniformly dispersed in plastic.
Technical indexes: Decomposition temperature: 205±3ºC
Amount of gas evolution: 225±5ml/g(STP)
Average particle size(D50): 9-10μm
Application: Common universal high temperature foaming agent. Widely used in plastics and rubber foam, such as PE(IXPE), PS, EVA , PVC, NBR, SBR, and rubber mixture. Especially suitable for PVC calendering and coating; Commonly used in molded PE, PVC extrusion and rubber molded foam; can be used for the MD injection of EVA and large and small mold pressing foam. Widely used in insulation materials, sports equipment handle and shoe material .
Packing: 25kg lined with plastic bag.
Storage: Good storage stability at room temperature. It should be stored in a cool & dry place, away from fire, sparks and heat. In case of fire, please use spray water, carbon dioxide or chemical powder for fire extinguishing, no artificial fight.